6 Unit and less / Short Span (Alpha-Bond/G)
Porperties
|
- Not deformative even at high temperature and has strong
bonding strength with ceramics.
- Either excellence in resisting corrosion and discoloration or bionic friendlinessdo
good for gingiva by diminishing plaque.
- Alpha-Bond/G and Alpha-Bond/H contains gold high and its beautiful gold
color satisfies sthetic requirements of the patients.
- Has high bonding strength with dental ceramics in the market and excellent
in casting. |
| Use |
Porcelain Crown & Bridge |
Composition and Properties
|
Alloy
|
Type
|
Composition(%)
|
Color
|
Hardness(VHN)
|
Elongation
(%)
|
Tensile Strength
(MPa)
|
Yield Strength
(MPa)
|
Melting point
(?)
|
|
Au
|
Pt
|
Pd
|
Ag
|
Soft
|
Hard
|
|
Alpha Bond/G
|
?/font>
|
87
|
9
|
1
|
-
|
Gold
|
?/font>
|
155
|
11
|
402
|
266
|
1110-1160
|
6 Unit and more / Long Span (Alpha-Bond/H, Alpha-Bond/W, Econo Bond-1,
Econo Bond-2)
Porperties
|
- Not deformative even at high temperature and has strong
bonding strength with ceramics.
- Either excellence in resisting corrosion and discoloration or bionic friendlinessdo
good for gingiva by diminishing plaque.
- Alpha-Bond/G and Alpha-Bond/H contains gold high and its beautiful gold
color satisfies sthetic requirements of the patients.
- Has high bonding strength with dental ceramics in the market and excellent
in casting. |
| Use |
Porcelain Crown & Bridge |
Composition and Properties
|
Alloy
|
Type
|
Composition(%)
|
Color
|
Hardness(VHN)
|
Elongation
(%)
|
Tensile Strength
(MPa)
|
Yield Strength
(MPa)
|
Melting point
(?)
|
|
Au
|
Pt
|
Pd
|
Ag
|
Soft
|
Hard
|
|
Alpha Bond/H
|
hard
|
85
|
8
|
5
|
-
|
Golden White
|
?/font>
|
173
|
7
|
450
|
270
|
1120-1175
|
|
Alpha Bond/W
|
extra hard
|
75
|
10
|
10
|
-
|
Silver White
|
?/font>
|
232
|
5
|
550
|
290
|
1135-1210
|
|
Econo Bond-1
|
Semi
|
52
|
-
|
31
|
4
|
Silver White
|
?/font>
|
265
|
11
|
843
|
447
|
1075-1194
|
|
Econo Bond-2
|
Semi
|
?/font>
|
-
|
55
|
35
|
Silver White
|
?/font>
|
273
|
8
|
890
|
585
|
1130-1210
|
|
|
|
|
| |
|
|
|